General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.16 g/cm³ Show Supplier Material materials with Densidad of 1.16 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.7 % Show Supplier Material materials with Moisture absorption of 0.7 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 200 % Show Supplier Material materials with Elongación of 200 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 500 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 500 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 1.2 GPa Show Supplier Material materials with Módulo de flexión of 1.2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 1.2 GPa Show Supplier Material materials with Módulo elástico of 1.2 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 53 MPa Show Supplier Material materials with Resistencia a la flexión of 53 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 36 MPa Show Supplier Material materials with Resistencia a la tracción of 36 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 69 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 69 kJ/m² | ISO 179/2C | 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 500 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 500 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 83 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 83 °C | ASTM D 648 | 6.4 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 74 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 74 °C | ASTM D 648 | 6.4 mm, unannealed |
Temperatura de flexión bajo carga | 74 - 83 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 74 - 83 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+11 - 5.00E+12 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+11 - 5.00E+12 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+11 - 5.00E+12 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+11 - 5.00E+12 Ω·cm | ASTM D 257 |
Óptico
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción of 0.6 % | SABIC method |
Contracción transversal | 23.0 °C | 0.6 % Show Supplier Material materials with Contracción transversal of 0.6 % | SABIC method |
Velocidad de flujo de la masa derretida | 19 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 19 g/10min | ASTM D 1238 | 260°C/2.16 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Semiconductor, Data Management | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 90 to 95.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |