Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.23 % Show Supplier Material materials with Absorción de agua of 0.23 % | ISO 62-1 | (23°C/24hrs) |
Densidad | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Densidad of 1.46 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.1 % Show Supplier Material materials with Elongación of 2.1 % | ISO 527 | break, 5 mm/min |
Módulo de flexión | 23.0 °C | 9.9 GPa Show Supplier Material materials with Módulo de flexión of 9.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 11.4 GPa Show Supplier Material materials with Módulo elástico of 11.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 200 MPa Show Supplier Material materials with Resistencia a la flexión of 200 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 130 MPa Show Supplier Material materials with Resistencia a la tracción of 130 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.1E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.4E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||||
Glow Wire Ignition Temperature | 850 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 850 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 275 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 275 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 258 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 258 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 140 °C Show Supplier Material materials with Relative temperature index, electrical of 140 °C | UL 746B | |||
Relative temperature index, mechanical impact | 140 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 140 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Temperatura de flexión bajo carga | 258 - 275 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 258 - 275 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284058- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103093686- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.41mm UL 94 <br> Glow Wire Flammability Index, 0.8 mm: 960°C IEC 60695-2-12 <br> Glow Wire Flammability Index, 1.6 mm: 960°C IEC 60695-2-12 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 0.41 mm Show Supplier Material materials with High Amp Arc Ignition of 0.41 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 0.41 mm Show Supplier Material materials with Hot-Wire Ignition of 0.41 mm | ≥, UL 746A | PLC 0 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Supplier Material materials with Índice de seguimiento comparativo of 0 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method | on tensile bar |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Circuit Protection, Additive Semiconductor Materials, Electronic Components, Enclosures, Wiring Devices | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120 to 140.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |