General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.3 % Show Supplier Material materials with Absorción de agua of 0.3 % | ISO 62-1 | (23°C/24hrs) |
Coefficient of friction | 0.51 - 0.57 [-] Show Supplier Material materials with Coefficient of friction of 0.51 - 0.57 [-] | ||
Coefficient of friction, kinetic | 0.51 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.51 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.57 [-] Show Supplier Material materials with Coefficient of friction, static of 0.57 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.58 g/cm³ Show Supplier Material materials with Densidad of 1.58 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.58 [-] Show Supplier Material materials with Densidad relativa of 1.58 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.3 % Show Supplier Material materials with Elongación of 2.3 % | ISO 527 | break, 5 mm/min |
Flexural strain | 23.0 °C | 4.8 % Show Supplier Material materials with Flexural strain of 4.8 % | ISO 178 | break, 2 mm/min, 180°C |
Impact strength, Izod notched, ASTM | 23.0 °C | 90 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 90 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 730 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 730 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, Total Energy of 8 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 10.1 GPa Show Supplier Material materials with Módulo de flexión of 10.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 11.5 GPa Show Supplier Material materials with Módulo elástico of 11.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 260 MPa Show Supplier Material materials with Resistencia a la flexión of 260 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 188 MPa Show Supplier Material materials with Resistencia a la tracción of 188 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 45 kJ/m² | ISO 180/1U | unnotched 80*10*4, -40°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Calor específico | 23.0 °C | 1722 J/(kg·K) Show Supplier Material materials with Calor específico of 1722 J/(kg·K) | ASTM E 1269 |
Coeficiente de dilatación térmica | 23.0 °C | 2.2E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.2E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.8E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Conductividad térmica | 23.0 °C | 0.24 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.24 W/(m·K) | ASTM D 5930 |
Heat deflection temperature, 0.45 MPa | 293 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 293 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 275 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 275 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 275 - 293 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 275 - 293 °C | ||
Temperatura de reblandecimiento Vicat | 258 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 258 °C | ISO 306 | Rate B/120 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method |
Contracción transversal | 23.0 °C | 0.8 % Show Supplier Material materials with Contracción transversal of 0.8 % | SABIC method |
Velocidad de flujo de la masa derretida | 28 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 28 g/10min | ASTM D 1238 | 340°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 24 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 24 cm³/10min | ISO 1133 | MVR at 340°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor, Laundry Dryer, Medical Device, Exhaust System, Forward Lighting, Engine Component, Electrical, EV Infrastructure, Gear/Bearing/Slider, Heavy Vehicles, Lawn/Garden, Electronic Components, Amusement Machine, Auto Aftermarket, Circuit Protection, Air Intake System, Building Element | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |