Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 4 % Show Supplier Material materials with Elongación of 4 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 645 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 645 J/m | ASTM D 256 | notched, 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 34 J Show Supplier Material materials with Instrumented Impact, at Peak of 34 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2 GPa Show Supplier Material materials with Módulo de flexión of 2 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 1.9 GPa Show Supplier Material materials with Módulo elástico of 1.9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 68 MPa Show Supplier Material materials with Resistencia a la flexión of 68 MPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 42 MPa Show Supplier Material materials with Resistencia a la tracción of 42 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 645 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 645 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 123 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 123 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 64 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 64 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 64 - 123 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 64 - 123 °C | ||
Temperatura de reblandecimiento Vicat | 136 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 136 °C | ASTM D 1525 | Rate B/120 | |
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104427473 - - <br> UL Recognized, 94HB Flame Class Rating: ≥0.75mm UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.2 % Show Supplier Material materials with Contracción of 1.2 % | SABIC method |
Contracción transversal | 23.0 °C | 1.2 % Show Supplier Material materials with Contracción transversal of 1.2 % | SABIC method |
Velocidad de flujo de la masa derretida | 11 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 11 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 10 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 10 cm³/10min | ASTM D 1238 | MVR at 250°C/5 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Healthcare | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |