Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad relativa | 23.0 °C | 1.1 [-] Show Supplier Material materials with Densidad relativa of 1.1 [-] | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 39 % Show Supplier Material materials with Elongación of 39 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 256 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 256 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 768 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 768 J/m | ASTM D 4812 | -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 15 J Show Supplier Material materials with Instrumented Impact, Total Energy of 15 J | ASTM D 3763 | -30°C |
Módulo de flexión | 23.0 °C | 2.7 GPa Show Supplier Material materials with Módulo de flexión of 2.7 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2 GPa Show Supplier Material materials with Módulo elástico of 2 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la flexión | 23.0 °C | 100 MPa Show Supplier Material materials with Resistencia a la flexión of 100 MPa | ASTM D 790 | yld, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 69 MPa Show Supplier Material materials with Resistencia a la tracción of 69 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 15 kJ/m² | ISO 180/1A | notched 80*10*4 |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.22E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.22E-4 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.42E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.42E-4 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 187 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 187 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 78 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 78 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 78 - 187 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 78 - 187 °C | ||
Temperatura de reblandecimiento Vicat | 203 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 203 °C | ISO 306 | Rate B/50 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.2 % Show Supplier Material materials with Contracción of 1.2 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción transversal of 1.1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 97 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 97 g/10min | ASTM D 1238 | 280°C/5.0 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Enclosures, Auto Electrical, Document Handling, Sensor, Ignition System, Personal Computing | |
| Availability | Asia,Americas | |
| Processing methods | Middle - Zone 2 Temperature: 260 to 295.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |