NORYL™ Resin FNH2160 - Americas

Want to keep this datasheet? Save it now in your required format

Description

NORYL™ FNH2160 resin is a foamable blend of polyphenylene ether (PPE) + high impact polystyrene (HIPS) and offers 20% weight reduction at 6.35mm (0.250”) wall. This material contains non-brominated, non-chlorinated flame retardant with a UL94 flame rating of 5VA at 3.9 mm and V1 at 3mm. NORYL FNH2160 resin offers fast cycle time, improved processing, and exhibits good dimensional stability and low moisture absorption. The unique combination of properties in this structural foam material allows for designing optimum wall thickness in computer and business machine applications, electrical enclosures/housings, medical equipment, and hospital bed rails and components.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Healthcare

Equipos médicos

Medical Equipment General

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Absorción de agua	23.0 °C	0.07 % Show Supplier Material materials with Absorción de agua of 0.07 %	ASTM D 570 \| (23°C/24hrs)
Densidad relativa	23.0 °C	1.12 [-] Show Supplier Material materials with Densidad relativa of 1.12 [-]	ASTM D 792

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	12 % Show Supplier Material materials with Elongación of 12 %	ASTM D 638 \| break, 6.35 mm
Instrumented Impact, at Peak	23.0 °C	29 J Show Supplier Material materials with Instrumented Impact, at Peak of 29 J	ASTM D 3763 \| 23°C
Módulo de flexión	23.0 °C	2.3 GPa Show Supplier Material materials with Módulo de flexión of 2.3 GPa	ASTM D 790 \| 6.4 mm
Módulo elástico	23.0 °C	2.7 GPa Show Supplier Material materials with Módulo elástico of 2.7 GPa	ASTM D 638 \| 50 mm/min
Resistencia a la flexión	23.0 °C	70 MPa Show Supplier Material materials with Resistencia a la flexión of 70 MPa	ASTM D 790 \| yield, 6.4 mm
Resistencia a la tracción	23.0 °C	34 MPa Show Supplier Material materials with Resistencia a la tracción of 34 MPa	ASTM D 638 \| break, 6.35 mm

Aplicaciones térmicas

Property	Value	Comment
Heat deflection temperature, 0.45 MPa	93 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 93 °C	ASTM D 648 \| 6.4 mm, unannealed
Heat deflection temperature, 1.80 MPa	82 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 82 °C	ASTM D 648 \| 6.4 mm, unannealed
Relative temperature index, electrical	65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C	UL 746B
Relative temperature index, mechanical impact	65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C	UL 746B
Relative temperature index, mechanical strength	65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C	UL 746B
Temperatura de flexión bajo carga	82 - 93 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 82 - 93 °C
Inflamabilidad	UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101920328- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥3.9mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥6mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥3mm UL 94

Rheological Properties

Property	Temperature	Value	Comment
Contracción	23.0 °C	0.5 % Show Supplier Material materials with Contracción of 0.5 %	SABIC method \| 6.4 mm
Velocidad de flujo del volumen derretido		36 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 36 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg

Technological properties

Property
Application areas	Lab Ware and Clinical Diagnostics, Medical Device, Monitoring and Imaging
Availability	Europe,Asia,Americas
Processing methods	Blowing Agent, Physical System: Nitrogen Gas- Concentration Range (Blowing Agent): 1 to 3.0% Recommended Concentration (Blowing Agent): 2% Drying Temperature (Resin): 70 to 80.0°C Drying Time (Resin): 2 to 4.0hrs Drying Time (Resin, Cumulative): 8hrs Melt Temperature: 270 to 310.0°C Nozzle Temperature: 270 to 305.0°C Front Temperature: 270 to 305.0°C Middle Temperature: 270 to 305.0°C Rear Temperature: 230 to 260.0°C Mold Temperature: 25 to 55.0°C
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.