Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.7 % Show Supplier Material materials with Absorción de agua of 0.7 % | ISO 62-1 | (23°C/24hrs) |
Densidad | 23.0 °C | 1.01 g/cm³ Show Supplier Material materials with Densidad of 1.01 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.1 % Show Supplier Material materials with Moisture absorption of 1.1 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Dureza Shore D | 23.0 °C | 61 [-] Show Supplier Material materials with Dureza Shore D of 61 [-] | ISO 868 | ||
Elongación | 23.0 °C | 50 % Show Supplier Material materials with Elongación of 50 % | ≥, ISO 527 | break, 50 mm/min | ||
Módulo elástico | 23.0 °C | 0.4 GPa Show Supplier Material materials with Módulo elástico of 0.4 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la tracción | 23.0 °C | 22 MPa Show Supplier Material materials with Resistencia a la tracción of 22 MPa | ISO 527 | yield, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 120 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 120 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm | ||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Aplicaciones térmicas
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Melt Temperature: 260°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |