Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.9 % Show Supplier Material materials with Absorción de agua of 0.9 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.34 [-] Show Supplier Material materials with Densidad relativa of 1.34 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.5 % Show Supplier Material materials with Moisture absorption of 0.5 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 64 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 64 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 8 J Show Supplier Material materials with Instrumented Impact, Total Energy of 8 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 6.9 GPa Show Supplier Material materials with Módulo de flexión of 6.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 9.5 GPa Show Supplier Material materials with Módulo elástico of 9.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 228 MPa Show Supplier Material materials with Resistencia a la flexión of 228 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 165 MPa Show Supplier Material materials with Resistencia a la tracción of 165 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 64 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 64 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 205 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 205 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 205 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 205 °C |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method | 3.2 mm |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Surgical Devices | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 150°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |