General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.433 g/cm³ Show Supplier Material materials with Densidad of 1.433 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.44 [-] Show Supplier Material materials with Densidad relativa of 1.44 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.11 % Show Supplier Material materials with Moisture absorption of 0.11 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.4 [-] | ASTM E 132 |
Dureza Rockwell M | 23.0 °C | 112 [-] Show Supplier Material materials with Dureza Rockwell M of 112 [-] | ASTM D 785 | |
Elongación | 23.0 °C | 0.9 % Show Supplier Material materials with Elongación of 0.9 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 64 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 64 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 560 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 560 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Módulo de cizallamiento | 23.0 °C | 4.7 GPa Show Supplier Material materials with Módulo de cizallamiento of 4.7 GPa | ASTM D732 |
Módulo de flexión | 23.0 °C | 30.6 GPa Show Supplier Material materials with Módulo de flexión of 30.6 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 35.5 GPa Show Supplier Material materials with Módulo elástico of 35.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la compresión | 23.0 °C | 218 MPa Show Supplier Material materials with Resistencia a la compresión of 218 MPa | SABIC method |
Resistencia a la flexión | 23.0 °C | 364 MPa Show Supplier Material materials with Resistencia a la flexión of 364 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 247 MPa Show Supplier Material materials with Resistencia a la tracción of 247 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 6 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 33 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Resistencia al cizallamiento | 23.0 °C | 120 MPa Show Supplier Material materials with Resistencia al cizallamiento of 120 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3E-6 1/K | ASTM E 831 | -40°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4E-5 1/K | ASTM E 831 | -40°C to 150°C |
Heat deflection temperature, 1.80 MPa | 193 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 193 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 193 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 193 °C |
Eléctrico
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | ASTM D 955 | 24 hrs |
Contracción transversal | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción transversal of 0.1 % | ASTM D 955 | 24 hrs |
Velocidad de flujo de la masa derretida | 40 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 40 g/10min | ASTM D 1238 | 380°C/6.7 kgf |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Maximum Moisture Content: 0.02% | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |