Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.4 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.4 [-] | ASTM E 132 |
Elongación | 23.0 °C | 2.3 % Show Supplier Material materials with Elongación of 2.3 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 109 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 109 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 711 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 711 J/m | ASTM D 4812 | 23°C |
Módulo de cizallamiento | 23.0 °C | 4.4 GPa Show Supplier Material materials with Módulo de cizallamiento of 4.4 GPa | ASTM D732 |
Módulo de flexión | 23.0 °C | 15.8 GPa Show Supplier Material materials with Módulo de flexión of 15.8 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 19.1 GPa Show Supplier Material materials with Módulo elástico of 19.1 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 344 MPa Show Supplier Material materials with Resistencia a la flexión of 344 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 245 MPa Show Supplier Material materials with Resistencia a la tracción of 245 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 109 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 109 kJ/m² | ASTM D 256 | notched, 23°C |
Resistencia al cizallamiento | 23.0 °C | 121.4 MPa Show Supplier Material materials with Resistencia al cizallamiento of 121.4 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.4E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.4E-6 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.5E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 170 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 170 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 170 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 170 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100000 - 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100000 - 1000000 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Aircraft Seating | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |