Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.2 % Show Supplier Material materials with Elongación of 1.2 % | ISO 527 | break, 5 mm/min |
Módulo de flexión | 23.0 °C | 2.8 GPa Show Supplier Material materials with Módulo de flexión of 2.8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo elástico of 2.6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 15 MPa Show Supplier Material materials with Resistencia a la flexión of 15 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 20 MPa Show Supplier Material materials with Resistencia a la tracción of 20 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 3.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 3.5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 5.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 5.5 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.3E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.3E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.5E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.5E-4 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature, 0.45 MPa | 100 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 100 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 60 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 60 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 60 - 100 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 60 - 100 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Dielectric constant, 100MHz | 23.0 °C | 13.6 [-] Show Supplier Material materials with Dielectric constant, 100MHz of 13.6 [-] | IEC 60250 | 100 MHz |
Dielectric constant, 1GHz | 23.0 °C | 13.1 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 13.1 [-] | IEC 60250 |
Dielectric constant, 500MHz | 23.0 °C | 13.4 [-] Show Supplier Material materials with Dielectric constant, 500MHz of 13.4 [-] | IEC 60250 |
Dissipation factor, 100MHz | 23.0 °C | 9E-3 [-] Show Supplier Material materials with Dissipation factor, 100MHz of 9E-3 [-] | IEC 60250 | 100 MHz |
Dissipation factor, 1GHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 8E-3 [-] | IEC 60250 |
Dissipation factor, 500MHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 500MHz of 8E-3 [-] | IEC 60250 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.5 % Show Supplier Material materials with Contracción of 1.5 % | SABIC method |
Velocidad de flujo del volumen derretido | 7.5 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 7.5 cm³/10min | ISO 1133 | MVR at 190°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosures | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |