Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Supplier Material materials with Absorción de agua of 0.08 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.34 g/cm³ Show Supplier Material materials with Densidad of 1.34 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.35 [-] Show Supplier Material materials with Densidad relativa of 1.35 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.08 % Show Supplier Material materials with Moisture absorption of 0.08 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 4.6 % Show Supplier Material materials with Elongación of 4.6 % | ISO 527 | yield, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 490 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 490 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 50 J Show Supplier Material materials with Instrumented Impact, Total Energy of 50 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.1 GPa Show Supplier Material materials with Módulo de flexión of 2.1 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo elástico of 2.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 73 MPa Show Supplier Material materials with Resistencia a la flexión of 73 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 48 MPa Show Supplier Material materials with Resistencia a la tracción of 48 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 34 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 34 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 31 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 31 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.16E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.16E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 9.74E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 9.74E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 122 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 122 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 95 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 95 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Supplier Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Temperatura de flexión bajo carga | 95 - 122 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 95 - 122 °C | ||||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating: 0.46mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.63mm UL 94 <br> UV-light, water exposure/immersion: F1- UL 746C <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104207620- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=104207621- - <br> UL Yellow Card Link 3: https://iq.ul.com/ul/cert.aspx?ULID=104244704- - <br> UL Yellow Card Link 4: https://iq.ul.com/ul/cert.aspx?ULID=104244705- - <br> UL Recognized, 94-5VA Flame Class Rating: ≥2.5mm UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 0.46 mm Show Supplier Material materials with High Amp Arc Ignition of 0.46 mm | ≥, UL 746A | PLC 4 |
High Volt Arc Track Rate | 23.0 °C | 4 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 4 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 0.63 mm Show Supplier Material materials with Hot-Wire Ignition of 0.63 mm | ≥, UL 746A | PLC 3 |
Índice de seguimiento comparativo | 23.0 °C | 2 V Show Supplier Material materials with Índice de seguimiento comparativo of 2 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción of 1.1 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 9.3 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 9.3 g/10min | ASTM D 1238 | 250°C/5.0 kgf | |
Velocidad de flujo del volumen derretido | 7 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 7 cm³/10min | ISO 1133 | MVR at 250°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Personal Computing, ATM/Ticket Machine, Enclosures | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |