General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad relativa | 23.0 °C | 1.08 [-] Show Supplier Material materials with Densidad relativa of 1.08 [-] | ASTM D 792 | |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 4.5 % Show Supplier Material materials with Elongación of 4.5 % | ISO 527 | yield, 50 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 510 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 510 J/m | ASTM D 256 | ||
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo elástico of 2.3 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 77 MPa Show Supplier Material materials with Resistencia a la flexión of 77 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 68 MPa Show Supplier Material materials with Resistencia a la tracción of 68 MPa | ISO 527 | yield, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 21 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 21 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 15.8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 15.8 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C | ||
Resistencia al choque, ensayo Charpy no entallado | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C | ||||
Resistencia al choque, ensayo Izod no entallado | ISO 180/1U | unnotched 80*10*4, -30°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 0.45 MPa | 146 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 146 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 121 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 121 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 121 - 146 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 121 - 146 °C | ||
Temperatura de reblandecimiento Vicat | 151 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 151 °C | ISO 306 | Rate B/50 | |
Inflamabilidad | UL Compliant, 94V-1 Flame Class Rating: 1.5mm UL 94 by SABIC-IP <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 1mm IEC 60695-2-12 <br> Smoke density, DS-max, 25 kW/m2, 1.5 mm: 47- ISO 5659-2 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción transversal of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 10.5 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 10.5 g/10min | ASTM D 1238 | 280°C/10.0 kgf | |
Velocidad de flujo del volumen derretido | 11 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 11 cm³/10min | ISO 1133 | MVR at 280°C/10.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Enclosure/Housing/Cover | |
Availability | Europe,Asia | |
Processing methods | Drying Temperature: 90 to 100.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |