Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.6 g/cm³ Show Supplier Material materials with Densidad of 1.6 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.64 [-] Show Supplier Material materials with Densidad relativa of 1.64 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.21 % Show Supplier Material materials with Moisture absorption of 0.21 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.6 % Show Supplier Material materials with Elongación of 1.6 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 82 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 82 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 291 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 291 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 5 J Show Supplier Material materials with Instrumented Impact, Total Energy of 5 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 15.9 GPa Show Supplier Material materials with Módulo de flexión of 15.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 18.9 GPa Show Supplier Material materials with Módulo elástico of 18.9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 314 MPa Show Supplier Material materials with Resistencia a la flexión of 314 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 227 MPa Show Supplier Material materials with Resistencia a la tracción of 227 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 34 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 34 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.8E-5 1/K | ASTM D 696 | -30°C to 30°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 3.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 3.5E-5 1/K | ASTM D 696 | -30°C to 30°C |
Heat deflection temperature, 0.45 MPa | 293 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 293 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 272 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 272 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 272 - 293 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 272 - 293 °C |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | ATM/Ticket Machine, Electronic Components, Enclosures | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 120 to 150.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |