General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.36 g/cm³ Show Supplier Material materials with Densidad of 1.36 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.1 % Show Supplier Material materials with Elongación of 2.1 % | ISO 527 | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 48 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 48 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 576 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 576 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 2 J Show Supplier Material materials with Instrumented Impact, at Peak of 2 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 10.3 GPa Show Supplier Material materials with Módulo de flexión of 10.3 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 11.5 GPa Show Supplier Material materials with Módulo elástico of 11.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 241 MPa Show Supplier Material materials with Resistencia a la flexión of 241 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 149 MPa Show Supplier Material materials with Resistencia a la tracción of 149 MPa | ISO 527 | break |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 13 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 13 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 212 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 212 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.63E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.63E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 4.12E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4.12E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 1.80 MPa | 246 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 246 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 246 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 246 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+6 - 1.00E+8 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+6 - 1.00E+8 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+6 - 1.00E+8 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+6 - 1.00E+8 Ω·cm | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Semiconductor, Data Management, Industrial Material Handling, Electronic Material Handling | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |