Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.04 g/cm³ Show Supplier Material materials with Densidad of 1.04 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.04 [-] Show Supplier Material materials with Densidad relativa of 1.04 [-] | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 25 % Show Supplier Material materials with Elongación of 25 % | ISO 527 | break, 50 mm/min |
Hardness, Rockwell R | 23.0 °C | 112 [-] Show Supplier Material materials with Hardness, Rockwell R of 112 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 320 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 320 J/m | ASTM D 256 |
Instrumented Impact, Total Energy | 23.0 °C | 30 J Show Supplier Material materials with Instrumented Impact, Total Energy of 30 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 70 MPa Show Supplier Material materials with Resistencia a la flexión of 70 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 35 MPa Show Supplier Material materials with Resistencia a la tracción of 35 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 26 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 26 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.82E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8.82E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8.82E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 94 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 94 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 81 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 81 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Temperatura de flexión bajo carga | 81 - 94 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 81 - 94 °C | ||||
Temperatura de reblandecimiento Vicat | 100 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 100 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103956404- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103956406- - <br> UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link 3: https://iq.ul.com/ul/cert.aspx?ULID=103938869- - | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 3 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 3 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | ≥, UL 746A | PLC 4 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Supplier Material materials with Índice de seguimiento comparativo of 0 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Melt viscosity | 23.0 °C | 225 Pa·s Show Supplier Material materials with Melt viscosity of 225 Pa·s | ASTM D 3825 | 240°C, 1000 sec-1 |
Velocidad de flujo de la masa derretida | 18 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 18 g/10min | ISO 1133 | 220°C/10.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80 to 95.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |