General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.07 % Show Supplier Material materials with Absorción de agua of 0.07 % | ISO 62-1 | (23°C/24hrs) |
Coefficient of friction | 0.35 [-] Show Supplier Material materials with Coefficient of friction of 0.35 [-] | ||
Coefficient of friction, kinetic | 0.35 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.35 [-] | ASTM D 3702 Modified: Manual | |
Densidad relativa | 23.0 °C | 1.2 [-] Show Supplier Material materials with Densidad relativa of 1.2 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.28 % Show Supplier Material materials with Moisture absorption of 0.28 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 45.2 % Show Supplier Material materials with Elongación of 45.2 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 614 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 614 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 2.2 GPa Show Supplier Material materials with Módulo de flexión of 2.2 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.1 GPa Show Supplier Material materials with Módulo elástico of 2.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 79 MPa Show Supplier Material materials with Resistencia a la flexión of 79 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 45.2 MPa Show Supplier Material materials with Resistencia a la tracción of 45.2 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 16.9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 16.9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 304.3 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 304.3 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 16.1 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 16.1 kJ/m² | ISO 180/1A | notched 80*10*4, -30°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 168.6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 168.6 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.08E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.08E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.95E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7.95E-5 1/K | ISO 11359-2 | 23°C to 80°C |
Heat deflection temperature, 1.80 MPa | 119.8 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 119.8 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 119.8 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 119.8 °C | ||
Temperatura de reblandecimiento Vicat | 145.95 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 145.95 °C | ISO 306 | Rate B/50 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.83 % Show Supplier Material materials with Contracción of 0.83 % | ASTM D 955 | 24 hrs |
Contracción transversal | 23.0 °C | 0.94 % Show Supplier Material materials with Contracción transversal of 0.94 % | ASTM D 955 | 24 hrs |
Velocidad de flujo de la masa derretida | 27.7 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 27.7 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 24.19 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 24.19 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,MEA,Americas,Global | |
Processing methods | Drying Time: 3 to 4.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |