General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.41 - 0.48 [-] Show Supplier Material materials with Coefficient of friction of 0.41 - 0.48 [-] | ||
Coefficient of friction, kinetic | 0.41 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.41 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.48 [-] Show Supplier Material materials with Coefficient of friction, static of 0.48 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.37 g/cm³ Show Supplier Material materials with Densidad of 1.37 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 5.1 % Show Supplier Material materials with Elongación of 5.1 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 192 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 192 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1500 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1500 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 31 J Show Supplier Material materials with Instrumented Impact, at Peak of 31 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo elástico of 2.6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 69 MPa Show Supplier Material materials with Resistencia a la flexión of 69 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 43 MPa Show Supplier Material materials with Resistencia a la tracción of 43 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 14 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 14 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 105 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 105 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.3E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 139 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 139 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 135 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 135 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 135 - 139 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 135 - 139 °C |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Surgical Devices | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |