General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.4 g/cm³ Show Supplier Material materials with Densidad of 1.4 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.5 % Show Supplier Material materials with Elongación of 2.5 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 80 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 80 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 450 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 450 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 6.4 GPa Show Supplier Material materials with Módulo de flexión of 6.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 6.9 GPa Show Supplier Material materials with Módulo elástico of 6.9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 130 MPa Show Supplier Material materials with Resistencia a la flexión of 130 MPa | ISO 178 | 2 mm/min |
Resistencia a la tracción | 23.0 °C | 86 MPa Show Supplier Material materials with Resistencia a la tracción of 86 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 26 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 26 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 0.45 MPa | 124 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 124 °C | ASTM D 648 | 3.2 mm, unannealed |
Heat deflection temperature, 1.80 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ASTM D 648 | 3.2mm, unannealed |
Temperatura de flexión bajo carga | 118 - 124 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 118 - 124 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica | 23.0 °C | 3.36 [-] Show Supplier Material materials with Constante dieléctrica of 3.36 [-] | SABIC method | 1.9 GHz |
Dielectric constant, 10GHz | 23.0 °C | 3.32 [-] Show Supplier Material materials with Dielectric constant, 10GHz of 3.32 [-] | SABIC method |
Dielectric constant, 1GHz | 23.0 °C | 3.37 [-] Show Supplier Material materials with Dielectric constant, 1GHz of 3.37 [-] | SABIC method | 1.1 GHz |
Dielectric constant, 5GHz | 23.0 °C | 3.35 [-] Show Supplier Material materials with Dielectric constant, 5GHz of 3.35 [-] | SABIC method |
Dissipation factor, 1GHz | 23.0 °C | 8E-3 [-] Show Supplier Material materials with Dissipation factor, 1GHz of 8E-3 [-] | SABIC method | |
Dissipation factor, 5GHz | 23.0 °C | 7E-3 [-] Show Supplier Material materials with Dissipation factor, 5GHz of 7E-3 [-] | SABIC method |
Factor de disipación | 23.0 °C | 5E-3 [-] Show Supplier Material materials with Factor de disipación of 5E-3 [-] | SABIC method |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method |
Contracción transversal | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción transversal of 0.2 % | SABIC method |
Velocidad de flujo de la masa derretida | 17 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 17 g/10min | ASTM D 1238 | 300°C/2.16 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Wearables, Personal Computing, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Time: 3 to 4.0hrs | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |