General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.26 g/cm³ Show Supplier Material materials with Densidad of 1.26 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.26 [-] Show Supplier Material materials with Densidad relativa of 1.26 [-] | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Elongación | 23.0 °C | 5.4 % Show Supplier Material materials with Elongación of 5.4 % | ISO 527 | break, 5 mm/min | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 153 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 153 J/m | ASTM D 256 | notched, 23°C | ||
Módulo de flexión | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo de flexión of 2.4 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 87 MPa Show Supplier Material materials with Resistencia a la flexión of 87 MPa | ISO 178 | 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 49 MPa Show Supplier Material materials with Resistencia a la tracción of 49 MPa | ISO 527 | break, 5 mm/min | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 12 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 12 kJ/m² | ISO 180/1A | 80*10*4, 23°C | ||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 116 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 116 kJ/m² | ISO 180/1U | 80*10*4, 23°C | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 5.8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.8E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.4E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 138 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 138 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 129 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 129 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 129 - 138 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 129 - 138 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102158629- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥2mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.6mm UL 94 |
Eléctrico
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Building Accessory | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |