General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.425 g/cm³ Show Supplier Material materials with Densidad of 1.425 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.2 % Show Supplier Material materials with Elongación of 2.2 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 128 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 128 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 537 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 537 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 8.4 GPa Show Supplier Material materials with Módulo de flexión of 8.4 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 9.4 GPa Show Supplier Material materials with Módulo elástico of 9.4 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 180 MPa Show Supplier Material materials with Resistencia a la flexión of 180 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 129 MPa Show Supplier Material materials with Resistencia a la tracción of 129 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 128 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 128 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.9E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Heat deflection temperature, 1.80 MPa | 119 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 119 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 119 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 119 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102832656- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.8mm UL 94 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | ASTM D 955 | 24 hrs |
Contracción transversal | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción transversal of 0.1 % | ASTM D 955 | 24 hrs |
Velocidad de flujo de la masa derretida | 27.3 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 27.3 g/10min | ASTM D 1238 | 300°C/2.16 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Personal Computing, Data Transfer, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |