Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.29 g/cm³ Show Supplier Material materials with Densidad of 1.29 g/cm³ | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Moisture absorption of 0.13 % | ISO 62 | (23°C / 50% RH) |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 11 % Show Supplier Material materials with Elongación of 11 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 61 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 61 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2160 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2160 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 2.9 GPa Show Supplier Material materials with Módulo de flexión of 2.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.9 GPa Show Supplier Material materials with Módulo elástico of 2.9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 112 MPa Show Supplier Material materials with Resistencia a la flexión of 112 MPa | ISO 178 | 2 mm/min |
Resistencia a la tracción | 23.0 °C | 58 MPa Show Supplier Material materials with Resistencia a la tracción of 58 MPa | ISO 527 | break, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A | 80*10*3, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 182 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 182 kJ/m² | ISO 180/1U | 80*10*3, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment |
|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6.3E-5 1/K | ASTM E 831 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM E 831 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 168 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 168 °C | ASTM D 648 | 3.2 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 155 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 155 - 168 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 155 - 168 °C |
Eléctrico
Rheological Properties
| Property | Value | Comment |
|---|---|---|
Velocidad de flujo del volumen derretido | 22.8 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 22.8 cm³/10min | ISO 1133 | MVR at 330°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Antenna | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 135°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |