Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.27 % Show Supplier Material materials with Absorción de agua of 0.27 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.18 g/cm³ Show Supplier Material materials with Densidad of 1.18 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.18 [-] Show Supplier Material materials with Densidad relativa of 1.18 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.13 % Show Supplier Material materials with Moisture absorption of 0.13 % | ISO 62 | (23°C / 50% RH) |
Specific volume | 23.0 °C | 0.85 cm³/g Show Supplier Material materials with Specific volume of 0.85 cm³/g | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Dureza Rockwell M | 23.0 °C | 90 [-] Show Supplier Material materials with Dureza Rockwell M of 90 [-] | ASTM D 785 | | ||
Elongación | 23.0 °C | 20 % Show Supplier Material materials with Elongación of 20 % | ISO 527 | break, 50 mm/min | ||
Hardness, Pencil test | H | ASTM D 3363 | 1kgf | |||
Hardness, Rockwell L | 23.0 °C | 110 [-] Show Supplier Material materials with Hardness, Rockwell L of 110 [-] | ASTM D 785 | ||
Impact strength, Izod notched, ASTM | 23.0 °C | 30 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 30 J/m | ASTM D 256 | ||
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C | ||
Módulo de flexión | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | 2 mm/min | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 110 MPa Show Supplier Material materials with Resistencia a la flexión of 110 MPa | ISO 178 | yield, 2 mm/min | ||
Resistencia a la tracción | 23.0 °C | 59 MPa Show Supplier Material materials with Resistencia a la tracción of 59 MPa | ISO 527 | break, 50 mm/min | ||
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 2.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 2.5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm, -30°C | ||
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 46 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 46 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm, -30°C | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 2 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 2 kJ/m² | ISO 180/1A | notched 80*10*3, -30°C | ||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 40 kJ/m² | ISO 180/1U | unnotched 80*10*3, -30°C | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C | ||||
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 0.45 MPa | 129 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 129 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 115 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 115 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 115 - 129 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 115 - 129 °C | ||||
Temperatura de reblandecimiento Vicat | 138 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 138 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=104234328- - <br> UL Recognized, 94HB Flame Class Rating: ≥0.6mm UL 94 | ||||
Óptico
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 15.4 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 15.4 g/10min | ASTM D 1238 | 300°C/1.2 kgf | |
Velocidad de flujo del volumen derretido | 14 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 14 cm³/10min | ISO 1133 | MVR at 300°C/1.2 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Cluster, City, Building Accessory, Auto Aftermarket, Audio, Air Conditioning, Fluid Delivery, Enclosures, Electronic Components, Wiring Devices, Wireless Communications, Medical Device, Personal Computing, Motorcycle, Non-LED Lighting | |
| Availability | Asia | |
| Processing methods | Drying Temperature: 120°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |