Description

FLEX NORYL™ WCV072 resin is a flexible, non-reinforced extrusion grade of Polyphenylene Ether (PPE) + Thermoplastic Elastomer (TPE) with a Shore D Hardness rating of 72. FLEX NORYL WCV072 resin was developed for evaluation in automotive wire + cable applications requiring ISO6722 Class A or B. It exhibits ultra-thin wall capability, good scratch abrasion and pinch resistance, high dimensional stability, low shrinkage and warpage, very low water absorption, chemical resistance, and good dielectric strength. Processing is typically conducted on standard extrusion equipment, and UL 1581 testing is conducted on 2.0mm wire with 0.12mm X 20 stranded copper conductor.

Los datos sobre este material han sido proporcionados por Sabic.

A menos que se indique lo contrario, todas las medidas corresponden a condiciones de temperatura ambiente. A menos que se indique lo contrario, se utilizan las unidades del SI.
Las normas armonizadas son similares a uno o varios estándares del proveedor. Es posible que algunas normas armonizadas se ajusten al estándar original, mientras que otras pueden quedar fuera de su alcance.

Ashby charts

See where falls on the material property chart for against in your materials selection and design process. Our Ashby charts are interactive with more technical data upon clicking. Sign up to get access to this premium feature for free.

All categories

Available suppliers

SABIC

MANUFACTURER, PROCESSOR AND DISTRIBUTOR

Additional services:

Our six Global Application Technology development hubs add value to our customers’ entire product development cycles in a wide range of industries. We provide our customers with advanced design, predictive engineering, testing, validation and processing services. Our COLORXPRESS™ services team provides global color matching and maintenance. Our Fast Formulation services provide initial assessments within five business days and custom-made samples typically in four to six weeks.

Usos

Ingeniería eléctrica

Automotriz

Piezas generales para vehículos

Exterior automotriz

Materiales de este proveedor

LNP™ THERMOCOMP™ Compound WF006H

LNP™ THERMOCOMP™ Compound PF00C - Europe

LNP™ THERMOCOMP™ Compound JF006E - Europe

LEXAN™ Copolymer FXE1414T - Americas

LNP™ ELCRES™ CRX9411

Ver todos los materiales de este proveedor

Propiedades

General

Property	Temperature	Value	Comment
Absorción de agua	23.0 °C	0.12 % Show Supplier Material materials with Absorción de agua of 0.12 %	ISO 62-1 \| (23°C/saturated)
Densidad	23.0 °C	1.03 g/cm³ Show Supplier Material materials with Densidad of 1.03 g/cm³	ISO 1183
Densidad relativa	23.0 °C	1.03 [-] Show Supplier Material materials with Densidad relativa of 1.03 [-]	ASTM D 792
Moisture absorption	23.0 °C	0.05 % Show Supplier Material materials with Moisture absorption of 0.05 %	ISO 62 \| (23°C / 50% RH)

Mecánica

Property	Temperature	Value	Comment
Elongación	23.0 °C	46 % Show Supplier Material materials with Elongación of 46 %	ISO 527 \| break, 50 mm/min
Impact strength, Izod notched, ASTM	23.0 °C	309 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 309 J/m	ASTM D 256
Instrumented Impact, Total Energy	23.0 °C	45 J Show Supplier Material materials with Instrumented Impact, Total Energy of 45 J	ASTM D 3763 \| 23°C
Módulo de flexión	23.0 °C	1.7 GPa Show Supplier Material materials with Módulo de flexión of 1.7 GPa	ISO 178 \| 2 mm/min
Módulo elástico	23.0 °C	1.8 GPa Show Supplier Material materials with Módulo elástico of 1.8 GPa	ISO 527 \| 1 mm/min
Resistencia a la flexión	23.0 °C	59 MPa Show Supplier Material materials with Resistencia a la flexión of 59 MPa	ISO 178 \| yield, 2 mm/min
Resistencia a la tracción	23.0 °C	44 MPa Show Supplier Material materials with Resistencia a la tracción of 44 MPa	ISO 527 \| yield, 50 mm/min
Resistencia al choque, ensayo Charpy entallado	23.0 °C	33 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 33 kJ/m²	ISO 179/1eA \| V-notch Edgew, 23°C, 80104 sp=62mm
Resistencia al choque, ensayo Izod entallado	23.0 °C	6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 6 kJ/m²	ISO 180/1A \| 80104, -30°C

Aplicaciones térmicas

Property	Temperature	Value	Comment
Coeficiente de dilatación térmica	23.0 °C	8.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.4E-5 1/K	ISO 11359-2 \| -40°C to 40°C
Coeficiente de dilatación térmica transversal	23.0 °C	1.11E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.11E-4 1/K	ISO 11359-2 \| -40°C to 40°C
Heat deflection temperature, 1.80 MPa		98 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 98 °C	ISO 75/Af \| Flatw 80104 sp=64mm
Temperatura de flexión bajo carga		98 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 98 °C
Temperatura de reblandecimiento Vicat		117 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 117 °C	ISO 306 \| Rate B/120

Rheological Properties

Property	Value	Comment
Velocidad de flujo de la masa derretida	13.8 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 13.8 g/10min	ASTM D 1238 \| 280°C/5.0 kgf
Velocidad de flujo del volumen derretido	13 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min	ISO 1133 \| MVR at 280°C/5.0 kg

Technological properties

Property
Application areas	Auto Electrical, Auto Aftermarket, Wire & cable
Availability	Europe,Asia,Americas
Processing methods	Head Zone Temperature: 250 to 285.0°C Drying Time (Cumulative): 12hrs Water Bath Temperature: 15 to 80.0°C Neck Temperature: 250 to 285.0°C Middle Zone Temperatures: 230 to 285.0°C Melt Temperature: 250 to 285.0°C Screw Speed: 15 to 40.0rpm Screen Pack: 150 to 100.0- Feed Zone Temperature: 210 to 260.0°C Drying Time: 4 to 6.0hrs Conductor Pre-heat Temperature: 80 to 150.0°C Die Temperature: 250 to 285.0°C Drying Temperature: 60 to 80.0°C Cross-head Temperature: 250 to 285.0°C Cooling Water Air Gap: 100 to 200.0mm Maximum Moisture Content: 0.02% Extruder Length/Diameter Ratio (L/D): 22:1 to 26:1-
Supplier Disclaimer	While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right.