General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.83 g/cm³ Show Supplier Material materials with Densidad of 1.83 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % | ISO 527 | break, 5 mm/min |
Hardness, Ball Indentation | 23.0 °C | 145 MPa Show Supplier Material materials with Hardness, Ball Indentation of 145 MPa | ISO 2039-1 | H358/30 |
Módulo de flexión | 23.0 °C | 7.4 GPa Show Supplier Material materials with Módulo de flexión of 7.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 8 GPa Show Supplier Material materials with Módulo elástico of 8 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 140 MPa Show Supplier Material materials with Resistencia a la flexión of 140 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 100 MPa Show Supplier Material materials with Resistencia a la tracción of 100 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 4 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 35 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 35 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 33 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Taber Abrasion | 23.0 °C | 76 mg/1000cy Show Supplier Material materials with Taber Abrasion of 76 mg/1000cy | SABIC method | CS-17, 1 kg |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | nan | IEC 60695-10-2 | 125°C +/- 2°C | |||
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 8E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 8E-5 1/K | ISO 11359-2 | 23°C to 150°C | ||
Conductividad térmica | 23.0 °C | 0.33 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.33 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 180 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 180 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Temperatura de flexión bajo carga | 180 - 220 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 180 - 220 °C | ||||
Temperatura de reblandecimiento Vicat | 220 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 220 °C | ISO 306 | Rate A/50 | |||
Inflamabilidad | Glow Wire Flammability Index 750°C, passes at: 3.2mm IEC 60695-2-12 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.5 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.5 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.6 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.6 [-] | IEC 60250 | 50/60 Hz |
Dissipation factor, 1MHz | 23.0 °C | 0.01 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.01 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 1E-3 [-] | IEC 60250 | 50/60 Hz |
Sheet resistivity, ROA | 23.0 °C | 1.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+15 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+15 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+15 Ω·cm | >, IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method | on tensile bar |
Velocidad de flujo del volumen derretido | 11 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 11 cm³/10min | ISO 1133 | MVR at 265°C/1.2 kg |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 110 to 120.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |