General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 5.5 % Show Supplier Material materials with Absorción de agua of 5.5 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.19 g/cm³ Show Supplier Material materials with Densidad of 1.19 g/cm³ | ISO 1183 |
Índice límite de óxigeno | 23.0 °C | 28 % Show Supplier Material materials with Índice límite de óxigeno of 28 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % | ISO 527 | break, 5 mm/min |
Hardness, Rockwell L | 23.0 °C | 105 [-] Show Supplier Material materials with Hardness, Rockwell L of 105 [-] | ISO 2039-2 |
Módulo de flexión | 23.0 °C | 10 GPa Show Supplier Material materials with Módulo de flexión of 10 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 13 GPa Show Supplier Material materials with Módulo elástico of 13 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 230 MPa Show Supplier Material materials with Resistencia a la flexión of 230 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 170 MPa Show Supplier Material materials with Resistencia a la tracción of 170 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.1E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.1E-4 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 0.45 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 252 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 250 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 250 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |||
Temperatura de flexión bajo carga | 250 - 252 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 250 - 252 °C | ||||
Temperatura de reblandecimiento Vicat | 255 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 255 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating: 1.6mm UL 94 by SABIC-IP |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 178000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 178000 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 178000 Ω·cm Show Supplier Material materials with Volume resistivity of 178000 Ω·cm | IEC 60093 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | SABIC method | on tensile bar |
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |