General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 6.5 % Show Supplier Material materials with Absorción de agua of 6.5 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.36 g/cm³ Show Supplier Material materials with Densidad of 1.36 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 1.53 % Show Supplier Material materials with Moisture absorption of 1.53 % | ISO 62 | (23°C / 50% RH) |
Índice límite de óxigeno | 23.0 °C | 25 % Show Supplier Material materials with Índice límite de óxigeno of 25 % |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 3.3 % Show Supplier Material materials with Elongación of 3.3 % | ISO 527 | break, 5 mm/min |
Hardness, Rockwell L | 23.0 °C | 112 [-] Show Supplier Material materials with Hardness, Rockwell L of 112 [-] | ISO 2039-2 |
Impact strength, Izod notched, ASTM | 23.0 °C | 117 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 117 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 827 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 827 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 9 J Show Supplier Material materials with Instrumented Impact, at Peak of 9 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 8 GPa Show Supplier Material materials with Módulo de flexión of 8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 9 GPa Show Supplier Material materials with Módulo elástico of 9 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 203 MPa Show Supplier Material materials with Resistencia a la flexión of 203 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 144 MPa Show Supplier Material materials with Resistencia a la tracción of 144 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Charpy no entallado | 23.0 °C | 75 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy no entallado of 75 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm, -30°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 11 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 55 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 55 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 3.06E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 3.06E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.72E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.72E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Conductividad térmica | 23.0 °C | 0.33 W/(m·K) Show Supplier Material materials with Conductividad térmica of 0.33 W/(m·K) | ISO 8302 | ||
Heat deflection temperature, 0.45 MPa | 220 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 220 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm | |||
Heat deflection temperature, 1.80 MPa | 203 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 203 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 203 - 220 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 203 - 220 °C | ||||
Temperatura de reblandecimiento Vicat | 215 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 215 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Compliant, 94HB Flame Class Rating: 1.5mm UL 94 by SABIC-IP <br> Glow Wire Flammability Index 650°C, passes at: 2mm IEC 60695-2-12 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.4 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.4 [-] | IEC 60250 |
Dielectric constant, 60Hz | 23.0 °C | 3.6 [-] Show Supplier Material materials with Dielectric constant, 60Hz of 3.6 [-] | IEC 60250 | 50/60 Hz |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | IEC 60250 |
Dissipation factor, 50Hz | 23.0 °C | 6.1E-3 [-] Show Supplier Material materials with Dissipation factor, 50Hz of 6.1E-3 [-] | IEC 60250 | 50/60 Hz |
Rigidez dieléctrica | 23.0 °C | 20 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 20 kV/mm | IEC 60243-1 | in oil, 3.2 mm, |
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | >, IEC 60093 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 500 V Show Supplier Material materials with Índice de seguimiento comparativo of 500 V | IEC 60112 | |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Lighting | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |