General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.38 - 0.47 [-] Show Supplier Material materials with Coefficient of friction of 0.38 - 0.47 [-] | ||
Coefficient of friction, kinetic | 0.47 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.47 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.38 [-] Show Supplier Material materials with Coefficient of friction, static of 0.38 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.71 g/cm³ Show Supplier Material materials with Densidad of 1.71 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.7 % Show Supplier Material materials with Elongación of 1.7 % | ASTM D 638 | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 461 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 461 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 12.8 GPa Show Supplier Material materials with Módulo de flexión of 12.8 GPa | ASTM D 790 |
Módulo elástico | 23.0 °C | 13.7 GPa Show Supplier Material materials with Módulo elástico of 13.7 GPa | ASTM D 638 | 50 mm/min |
Resistencia a la flexión | 23.0 °C | 227 MPa Show Supplier Material materials with Resistencia a la flexión of 227 MPa | ASTM D 790 |
Resistencia a la tracción | 23.0 °C | 162 MPa Show Supplier Material materials with Resistencia a la tracción of 162 MPa | ASTM D 638 | break |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 85 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 85 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 273 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 273 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 273 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 273 °C | ||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103093683- - |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Document Handling | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |