Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Densidad of 1.44 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 2.7 % Show Supplier Material materials with Elongación of 2.7 % | ISO 527 | break, 5 mm/min |
Flexural strain | 23.0 °C | 4.5 % Show Supplier Material materials with Flexural strain of 4.5 % | ISO 178 | break, 2 mm/min |
Módulo de flexión | 23.0 °C | 2.7 GPa Show Supplier Material materials with Módulo de flexión of 2.7 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo elástico of 3.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 83 MPa Show Supplier Material materials with Resistencia a la flexión of 83 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 51 MPa Show Supplier Material materials with Resistencia a la tracción of 51 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 3 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 15 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 15 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 7.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 7.3E-5 1/K | ISO 11359-2 | 23°C to 60°C | ||
Heat deflection temperature, 0.45 MPa | 149 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 149 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 89 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 89 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 89 - 149 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 89 - 149 °C | ||||
Inflamabilidad | UL Compliant, 94V-0 Flame Class Rating: 3mm UL 94 by SABIC-IP | ||||
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.3 % Show Supplier Material materials with Contracción of 1.3 % | SABIC method |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Document Handling | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |