Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.2 % Show Supplier Material materials with Absorción de agua of 0.2 % | ISO 62-1 | (23°C/saturated) |
Densidad relativa | 23.0 °C | 1.2 [-] Show Supplier Material materials with Densidad relativa of 1.2 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.1 % Show Supplier Material materials with Moisture absorption of 0.1 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 90 % Show Supplier Material materials with Elongación of 90 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 190 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 190 J/m | ASTM D 256 | notched, -30°C |
Instrumented Impact, Total Energy | 23.0 °C | 60 J Show Supplier Material materials with Instrumented Impact, Total Energy of 60 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 98 MPa Show Supplier Material materials with Resistencia a la flexión of 98 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 62 MPa Show Supplier Material materials with Resistencia a la tracción of 62 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 37 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 37 kJ/m² | ISO 179/1eA | 80*10*4mm, Cut, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 11 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 11 kJ/m² | ISO 180/1A | 80*10*4, 0°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Ball Pressure Test | Pass | IEC 60695-10-2 | 75°C +/- 2°C | |||
Coeficiente de dilatación térmica | 23.0 °C | 5.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 5.9E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.9E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.9E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Ignition Temperature | 825 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C | IEC 60695-2-13 | 3.0 mm | |||
Heat deflection temperature, 0.45 MPa | 103 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 103 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 93 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 93 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 93 - 103 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 93 - 103 °C | ||||
Temperatura de reblandecimiento Vicat | 112 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 112 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Recognized, 94V-0 Flame Class Rating: ≥0.5mm UL 94 <br> Glow Wire Flammability Index 960°C, passes at: 0.75mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 0.75mm IEC 60695-2-12 <br> Glow Wire Ignitability Temperature, 1.5 mm: 825°C IEC 60695-2-13 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.2mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥0.2mm UL 94 <br> Glow Wire Ignitability Temperature, 1.0 mm: 800°C IEC 60695-2-13 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=102078504- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 2.00E+15 Ω Show Supplier Material materials with Sheet resistivity, ROA of 2.00E+15 Ω | >, ASTM D 257 |
Volume resistivity | 23.0 °C | 1.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 1.00E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 18 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 18 g/10min | ASTM D 1238 | 260°C/2.16 kgf | |
Velocidad de flujo del volumen derretido | 18 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 18 cm³/10min | ISO 1133 | MVR at 260°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Power Manangement, Watch/Jewelry, Wireless Communications | |
Availability | Asia | |
Processing methods | Nozzle Temperature: 250 to 300.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |