Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Absorción de agua | 23.0 °C | 0.18 % Show Supplier Material materials with Absorción de agua of 0.18 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.11 g/cm³ Show Supplier Material materials with Densidad of 1.11 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.11 [-] Show Supplier Material materials with Densidad relativa of 1.11 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.05 % Show Supplier Material materials with Moisture absorption of 0.05 % | ISO 62 | (23°C / 50% RH) |
Índice límite de óxigeno | 23.0 °C | 30 % Show Supplier Material materials with Índice límite de óxigeno of 30 % |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 3.5 % Show Supplier Material materials with Elongación of 3.5 % | ISO 527 | yield, 50 mm/min |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo de flexión of 2.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.5 GPa Show Supplier Material materials with Módulo elástico of 2.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 87 MPa Show Supplier Material materials with Resistencia a la flexión of 87 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 58 MPa Show Supplier Material materials with Resistencia a la tracción of 58 MPa | ISO 527 | yield, 50 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 6 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 6 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8.3E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7.7E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Glow Wire Ignition Temperature | 725 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 725 °C | IEC 60695-2-13 | 2.0 mm | |||
Heat deflection temperature, 1.80 MPa | 85 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 85 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Temperatura de flexión bajo carga | 85 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 85 °C | ||||
Temperatura de reblandecimiento Vicat | 105 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 105 °C | ISO 306 | Rate B/50 | |||
Inflamabilidad | Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12 <br> Glow Wire Flammability Index 960°C, passes at: 3mm IEC 60695-2-12 <br> UL Recognized, 94V-1 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-0 Flame Class Rating: ≥2mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101271387- - <br> Glow Wire Ignitability Temperature, 1.0 mm: 700°C IEC 60695-2-13 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 2.8 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 2.8 [-] | IEC 60250 |
Dissipation factor, 1MHz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 2E-3 [-] | IEC 60250 |
Rigidez dieléctrica | 23.0 °C | 27.5 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 27.5 kV/mm | IEC 60243-1 | in oil, 1.6 mm |
Sheet resistivity, ROA | 23.0 °C | 8.00E+16 - 8.50E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 8.00E+16 - 8.50E+16 Ω | IEC 60093 |
Volume resistivity | 23.0 °C | 3.00E+16 - 3.50E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 3.00E+16 - 3.50E+16 Ω·cm | IEC 60093 |
Índice de seguimiento comparativo | 23.0 °C | 250 V Show Supplier Material materials with Índice de seguimiento comparativo of 250 V | IEC 60112 | |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | SABIC method | 3.2 mm |
Velocidad de flujo del volumen derretido | 44 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 44 cm³/10min | ISO 1133 | MVR at 280°C/2.16 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Displays | |
| Availability | Americas | |
| Processing methods | Drying Temperature: 70 to 80.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |