General
Property | Temperature | Value | Comment |
---|---|---|---|
Coefficient of friction | 0.31 - 0.36 [-] Show Supplier Material materials with Coefficient of friction of 0.31 - 0.36 [-] | ||
Coefficient of friction, kinetic | 0.36 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.36 [-] | ASTM D 3702 Modified: Manual | |
Coefficient of friction, static | 0.31 [-] Show Supplier Material materials with Coefficient of friction, static of 0.31 [-] | ASTM D 3702 Modified: Manual | |
Densidad | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Densidad of 1.46 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.32 % Show Supplier Material materials with Moisture absorption of 0.32 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1 % Show Supplier Material materials with Elongación of 1 % | ISO 527 | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 32 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 32 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 128 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 128 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, at Peak of 7 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 8.3 GPa Show Supplier Material materials with Módulo de flexión of 8.3 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 10.2 GPa Show Supplier Material materials with Módulo elástico of 10.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 106 MPa Show Supplier Material materials with Resistencia a la flexión of 106 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 74 MPa Show Supplier Material materials with Resistencia a la tracción of 74 MPa | ISO 527 | break |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 3 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 3 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 17 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 17 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 155 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 155 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Temperatura de flexión bajo carga | 155 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 155 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 10 - 10000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 10000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 10 - 10000 Ω·cm Show Supplier Material materials with Volume resistivity of 10 - 10000 Ω·cm | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | ATM/Ticket Machine | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |