General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.46 g/cm³ Show Supplier Material materials with Densidad of 1.46 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.46 [-] Show Supplier Material materials with Densidad relativa of 1.46 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.27 % Show Supplier Material materials with Moisture absorption of 0.27 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 4.3 % Show Supplier Material materials with Elongación of 4.3 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 34 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 34 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 485 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 485 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 4.3 GPa Show Supplier Material materials with Módulo de flexión of 4.3 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 4.3 GPa Show Supplier Material materials with Módulo elástico of 4.3 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 155 MPa Show Supplier Material materials with Resistencia a la flexión of 155 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 98 MPa Show Supplier Material materials with Resistencia a la tracción of 98 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 33 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 33 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4E-5 1/K | ASTM D 696 | -30°C to 30°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 4.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4.4E-5 1/K | ASTM D 696 | -30°C to 30°C |
Heat deflection temperature, 0.45 MPa | 194 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 194 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 177 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 177 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 177 - 194 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 177 - 194 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 10 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 1000 Ω | ASTM D 257 |
Shielding effectiveness | 23.0 °C | 60 dB Show Supplier Material materials with Shielding effectiveness of 60 dB | SABIC method | @ 2.5mm |
Volume resistivity | 23.0 °C | 89 Ω·cm Show Supplier Material materials with Volume resistivity of 89 Ω·cm | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wireless Communications, Data Transfer | |
Availability | Europe,Asia,Americas | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |