Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.08 % Show Supplier Material materials with Absorción de agua of 0.08 % | ASTM D 570 | (23°C/24hrs) |
Densidad relativa | 23.0 °C | 1.31 [-] Show Supplier Material materials with Densidad relativa of 1.31 [-] | ASTM D 792 |
Specific volume | 23.0 °C | 0.76 cm³/g Show Supplier Material materials with Specific volume of 0.76 cm³/g | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 200 % Show Supplier Material materials with Elongación of 200 % | ASTM D 638 | brk, Type I, 50 mm/min |
Gardner Impact | 23.0 °C | 40 J Show Supplier Material materials with Gardner Impact of 40 J | ASTM D 3029 | modified, 23°C |
Hardness, Rockwell R | 23.0 °C | 117 [-] Show Supplier Material materials with Hardness, Rockwell R of 117 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 53 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 53 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1602 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1602 J/m | ASTM D 4812 | 23°C |
Módulo de flexión | 23.0 °C | 2.3 GPa Show Supplier Material materials with Módulo de flexión of 2.3 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la flexión | 23.0 °C | 82 MPa Show Supplier Material materials with Resistencia a la flexión of 82 MPa | ASTM D 790 | yld, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 51 MPa Show Supplier Material materials with Resistencia a la tracción of 51 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 53 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 53 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.39E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.39E-4 1/K | ASTM E 831 | 60°C to 138°C | ||
Heat deflection temperature, 0.45 MPa | 154 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 154 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 54 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 54 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 120 °C Show Supplier Material materials with Relative temperature index, electrical of 120 °C | UL 746B | |||
Relative temperature index, mechanical impact | 120 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 120 °C | UL 746B | |||
Relative temperature index, mechanical strength | 140 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 140 °C | UL 746B | |||
Temperatura de flexión bajo carga | 54 - 154 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 54 - 154 °C | ||||
Inflamabilidad | UL Recognized, 94HB Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=103938350- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.1 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.1 [-] | ASTM D 150 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.3 [-] Show Supplier Material materials with Constante dieléctrica, 100 Hz of 3.3 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 2E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 |
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 0 |
High Volt Arc Track Rate | 23.0 °C | 1 PLC Code Show Supplier Material materials with High Volt Arc Track Rate of 1 PLC Code | UL 746A | (PLC) |
Hot-Wire Ignition | 23.0 °C | 6 mm Show Supplier Material materials with Hot-Wire Ignition of 6 mm | ≥, UL 746A | PLC 2 |
Rigidez dieléctrica | 23.0 °C | 15.7 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 15.7 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Volume resistivity | 23.0 °C | 4.00E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 4.00E+16 Ω·cm | >, ASTM D 257 |
Índice de seguimiento comparativo | 23.0 °C | 0 V Show Supplier Material materials with Índice de seguimiento comparativo of 0 V | UL 746A | (UL) {PLC} |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 1.5 % Show Supplier Material materials with Contracción of 1.5 % | SABIC method | 2.3-4.6 mm |
Contracción transversal | 23.0 °C | 1.6 % Show Supplier Material materials with Contracción transversal of 1.6 % | SABIC method | 2.3-4.6 mm |
Melt viscosity | 23.0 °C | 600 Pa·s Show Supplier Material materials with Melt viscosity of 600 Pa·s | SABIC method |
Technological properties
Property | ||
---|---|---|
Availability | Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |