Propiedades
General
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 10 - 15 % Show Supplier Material materials with Elongación of 10 - 15 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 117.5 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 117.5 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 3.1 GPa Show Supplier Material materials with Módulo de flexión of 3.1 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la flexión | 23.0 °C | 97 MPa Show Supplier Material materials with Resistencia a la flexión of 97 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 52 MPa Show Supplier Material materials with Resistencia a la tracción of 52 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 117.5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 117.5 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 1.1 % Show Supplier Material materials with Contracción of 1.1 % | SABIC method | 48 hrs @ 23°C |
Technological properties
| Property | ||
|---|---|---|
| Availability | Europe,Asia,Americas | |
| Processing methods | Melt Temperature: 248 to 276.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |