Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad relativa | 23.0 °C | 1.32 [-] Show Supplier Material materials with Densidad relativa of 1.32 [-] | ASTM D 792 | |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 5.1 % Show Supplier Material materials with Elongación of 5.1 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 416 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 416 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 6 J Show Supplier Material materials with Instrumented Impact, Total Energy of 6 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 8.3 GPa Show Supplier Material materials with Módulo de flexión of 8.3 GPa | ASTM D 790 | 2.6 mm/min, 100 mm span |
Módulo elástico | 23.0 °C | 8.1 GPa Show Supplier Material materials with Módulo elástico of 8.1 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 193 MPa Show Supplier Material materials with Resistencia a la flexión of 193 MPa | ASTM D 790 | brk, 2.6 mm/min, 100 mm span |
Resistencia a la tracción | 23.0 °C | 131 MPa Show Supplier Material materials with Resistencia a la tracción of 131 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 37 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 37 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.44E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.44E-5 1/K | ASTM E 831 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 3.96E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 3.96E-5 1/K | ASTM E 831 | -20°C to 150°C | ||
Heat deflection temperature, 0.45 MPa | 213 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 213 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 208 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 208 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 105 °C Show Supplier Material materials with Relative temperature index, electrical of 105 °C | UL 746B | |||
Relative temperature index, mechanical impact | 105 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 105 °C | UL 746B | |||
Relative temperature index, mechanical strength | 105 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 105 °C | UL 746B | |||
Temperatura de flexión bajo carga | 208 - 213 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 208 - 213 °C | ||||
Temperatura de reblandecimiento Vicat | 214 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 214 °C | ASTM D 1525 | Rate B/50 | |||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221123- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | ≥, UL 746A | PLC 2 |
Hot-Wire Ignition | 23.0 °C | 3 mm Show Supplier Material materials with Hot-Wire Ignition of 3 mm | ≥, UL 746A | PLC 2 |
Sheet resistivity, ROA | 23.0 °C | 200000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 200000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 400 Ω·cm Show Supplier Material materials with Volume resistivity of 400 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.12 % Show Supplier Material materials with Contracción of 0.12 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.3 % Show Supplier Material materials with Contracción transversal of 0.3 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 7.5 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 7.5 g/10min | ASTM D 1238 | 337°C/6.6 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Wireless Communications, Commercial Appliance | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 150°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |