General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.23 g/cm³ Show Supplier Material materials with Densidad of 1.23 g/cm³ | ISO 1183 |
Moisture absorption | 23.0 °C | 0.16 % Show Supplier Material materials with Moisture absorption of 0.16 % | ASTM D 570 | (23°C/50% RH/24 hrs) |
Mecánica
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Impact strength, Izod notched, ASTM | 23.0 °C | 101 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 101 J/m | ASTM D 256 | notched, 23°C | ||
Instrumented Impact, at Peak | 23.0 °C | 41 J Show Supplier Material materials with Instrumented Impact, at Peak of 41 J | ASTM D 3763 | 23°C | ||
Módulo de flexión | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | ||
Módulo elástico | 23.0 °C | 2.4 GPa Show Supplier Material materials with Módulo elástico of 2.4 GPa | ISO 527 | 1 mm/min | ||
Resistencia a la flexión | 23.0 °C | 90 MPa Show Supplier Material materials with Resistencia a la flexión of 90 MPa | ISO 178 | ||
Resistencia a la tracción | 23.0 °C | 46 MPa Show Supplier Material materials with Resistencia a la tracción of 46 MPa | ISO 527 | break | ||
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C | ||
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 137 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 137 kJ/m² | ISO 180/1U | unnotched 80*10*4 | ||
Impact strength, Izod unnotched, ASTM | ASTM D 4812 | 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 6.55E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 6.55E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.6E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 140 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 140 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 127 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 127 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 127 - 140 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 127 - 140 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101343437- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.5mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1.5mm UL 94 <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=103093544- - |
Eléctrico
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Data Management, Vending Machine | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |