General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Dureza Rockwell M | 23.0 °C | 90 [-] Show Supplier Material materials with Dureza Rockwell M of 90 [-] | ASTM D 785 | |
Elongación | 23.0 °C | 4 - 6 % Show Supplier Material materials with Elongación of 4 - 6 % | SABIC - Japan Method | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 68 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 68 J/m | ASTM D 256 | notched, 23°C |
Módulo de flexión | 23.0 °C | 10.3 GPa Show Supplier Material materials with Módulo de flexión of 10.3 GPa | ASTM D 790 |
Resistencia a la flexión | 23.0 °C | 154 MPa Show Supplier Material materials with Resistencia a la flexión of 154 MPa | ASTM D 790 |
Resistencia a la tracción | 23.0 °C | 116 MPa Show Supplier Material materials with Resistencia a la tracción of 116 MPa | SABIC - Japan Method | yield |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 68 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 68 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.1E-5 - 3.3E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.1E-5 - 3.3E-5 1/K | TMA | -30°C to 30°C | ||
Heat deflection temperature, 1.80 MPa | 125 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 125 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Temperatura de flexión bajo carga | 125 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 125 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228551- - |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.00E+16 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.00E+16 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.15 % Show Supplier Material materials with Contracción of 0.15 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 15.4 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 15.4 g/10min | ASTM D 1238 | 300°C/2.16 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Small Appliance, Power Manangement, Wireless Communications, Building Accessory, Document Handling, Displays, Electronic Components, Enclosures | |
Availability | Europe,Asia,MEA,Americas | |
Processing methods | Back Pressure: 0.3 to 0.7MPa | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |