Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad relativa | 23.0 °C | 1.25 [-] Show Supplier Material materials with Densidad relativa of 1.25 [-] | ASTM D 792 | |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.9 % Show Supplier Material materials with Elongación of 1.9 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 37 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 37 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 347 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 347 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 82 J Show Supplier Material materials with Instrumented Impact, Total Energy of 82 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 6.4 GPa Show Supplier Material materials with Módulo de flexión of 6.4 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 7.5 GPa Show Supplier Material materials with Módulo elástico of 7.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 145 MPa Show Supplier Material materials with Resistencia a la flexión of 145 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 95 MPa Show Supplier Material materials with Resistencia a la tracción of 95 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 4 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 4 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 21 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 21 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.6E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.6E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 7.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 7.4E-5 1/K | ISO 11359-2 | 23°C to 80°C | ||
Heat deflection temperature, 0.45 MPa | 97 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 97 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 92 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 92 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 60 °C Show Supplier Material materials with Relative temperature index, electrical of 60 °C | UL 746B | |||
Relative temperature index, mechanical impact | 60 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 60 °C | UL 746B | |||
Relative temperature index, mechanical strength | 60 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 60 °C | UL 746B | |||
Temperatura de flexión bajo carga | 92 - 97 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 92 - 97 °C | ||||
Temperatura de reblandecimiento Vicat | 101 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 101 °C | ISO 306 | Rate B/120 | |||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=221061- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101632098- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94-5VB Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 800°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1 mm Show Supplier Material materials with High Amp Arc Ignition of 1 mm | ≥, UL 746A | PLC 0 |
Hot-Wire Ignition | 23.0 °C | 1 mm Show Supplier Material materials with Hot-Wire Ignition of 1 mm | ≥, UL 746A | PLC 0 |
Sheet resistivity, ROA | 23.0 °C | 1000000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1000000 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1000 Ω·cm Show Supplier Material materials with Volume resistivity of 1000 Ω·cm | ASTM D 257 |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.1 % Show Supplier Material materials with Contracción of 0.1 % | SABIC method | 3.2 mm |
Contracción transversal | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción transversal of 0.2 % | SABIC method | 3.2 mm |
Velocidad de flujo de la masa derretida | 17 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 17 g/10min | ASTM D 1238 | 260°C/2.16 kgf |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Electronic Components, Wiring Devices, Vacuum Cleaner | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 75 to 80.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |