General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 3 % Show Supplier Material materials with Elongación of 3 % | ISO 527 | break |
Impact strength, Izod notched, ASTM | 23.0 °C | 181 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 181 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 550 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 550 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 18 J Show Supplier Material materials with Instrumented Impact, at Peak of 18 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 4.6 GPa Show Supplier Material materials with Módulo de flexión of 4.6 GPa | ISO 178 |
Módulo elástico | 23.0 °C | 4.5 GPa Show Supplier Material materials with Módulo elástico of 4.5 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 127 MPa Show Supplier Material materials with Resistencia a la flexión of 127 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 74 MPa Show Supplier Material materials with Resistencia a la tracción of 74 MPa | ISO 527 | break |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 9 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 9 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 38 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 38 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 4.48E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 4.48E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 4.99E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4.99E-5 1/K | ISO 11359-2 | -40°C to 40°C | ||
Heat deflection temperature, 0.45 MPa | 146 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 146 °C | ASTM D 648 | 3.2 mm, unannealed | |||
Heat deflection temperature, 1.80 MPa | 141 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 141 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Temperatura de flexión bajo carga | 141 - 146 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 141 - 146 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284270- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=101284354- - <br> UL Recognized, 94V-0 Flame Class Rating: 1.7mm UL 94 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Wearables, Aircraft Seating, Air Cabin Interiors, Document Handling, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |