| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad relativa | 23.0 °C | 1.32 [-] Show Supplier Material materials with Densidad relativa of 1.32 [-] | ASTM D 792 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Elongación | 23.0 °C | 1.5 % Show Supplier Material materials with Elongación of 1.5 % | ASTM D 638 | brk, Type I, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 70 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 70 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 500 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 500 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 18 GPa Show Supplier Material materials with Módulo de flexión of 18 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Módulo elástico | 23.0 °C | 21 GPa Show Supplier Material materials with Módulo elástico of 21 GPa | ASTM D 638 | 5 mm/min |
Resistencia a la flexión | 23.0 °C | 260 MPa Show Supplier Material materials with Resistencia a la flexión of 260 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 185 MPa Show Supplier Material materials with Resistencia a la tracción of 185 MPa | ASTM D 638 | brk, Type I, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 70 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 70 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
| Property | Temperature | Value | Comment | ||
|---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 1.4E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 1.4E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 3.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 3.5E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature, 1.80 MPa | 86 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 86 °C | ASTM D 648 | 3.2mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 86 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 86 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101712652- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥0.8mm UL 94 <br> UL Recognized, 94V-1 Flame Class Rating: ≥0.7mm UL 94 | ||||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.40E+6 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.40E+6 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 3.19E+6 Ω·cm Show Supplier Material materials with Volume resistivity of 3.19E+6 Ω·cm | ASTM D 257 |
Rheological Properties
Technological properties
| Property | ||
|---|---|---|
| Application areas | Personal Computing | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 70°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |