General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.4 g/cm³ Show Supplier Material materials with Densidad of 1.4 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.4 [-] Show Supplier Material materials with Densidad relativa of 1.4 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.89 % Show Supplier Material materials with Moisture absorption of 0.89 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2.7 % Show Supplier Material materials with Elongación of 2.7 % | ISO 527 | yield, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 107 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 107 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 1100 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 1100 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 9 J Show Supplier Material materials with Instrumented Impact, Total Energy of 9 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 10 GPa Show Supplier Material materials with Módulo de flexión of 10 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 11.6 GPa Show Supplier Material materials with Módulo elástico of 11.6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 275 MPa Show Supplier Material materials with Resistencia a la flexión of 275 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 183 MPa Show Supplier Material materials with Resistencia a la tracción of 183 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 10 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 10 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 61 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 61 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.5E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 6.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 6.7E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature, 0.45 MPa | 257 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 257 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |||
Heat deflection temperature, 1.80 MPa | 246 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 246 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |||
Relative temperature index, electrical | 65 °C Show Supplier Material materials with Relative temperature index, electrical of 65 °C | UL 746B | |||
Relative temperature index, mechanical impact | 65 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 65 °C | UL 746B | |||
Relative temperature index, mechanical strength | 65 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 65 °C | UL 746B | |||
Temperatura de flexión bajo carga | 246 - 257 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 246 - 257 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101282588- - <br> UL Recognized, 94HB Flame Class Rating: 1.5mm UL 94 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Medical Device | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 80°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |