General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de Poisson | 23.0 °C | 0.5 [-] Show Supplier Material materials with Coeficiente de Poisson of 0.5 [-] | ASTM E 132 |
Elongación | 23.0 °C | 1.1 % Show Supplier Material materials with Elongación of 1.1 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 77 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 77 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 768 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 768 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 7 J Show Supplier Material materials with Instrumented Impact, Total Energy of 7 J | ASTM D 3763 | 23°C |
Módulo de cizallamiento | 23.0 °C | 5.2 GPa Show Supplier Material materials with Módulo de cizallamiento of 5.2 GPa | ASTM D732 |
Módulo de flexión | 23.0 °C | 40.7 GPa Show Supplier Material materials with Módulo de flexión of 40.7 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 47.4 GPa Show Supplier Material materials with Módulo elástico of 47.4 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 473 MPa Show Supplier Material materials with Resistencia a la flexión of 473 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 320 MPa Show Supplier Material materials with Resistencia a la tracción of 320 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 77 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 77 kJ/m² | ASTM D 256 | notched, 23°C |
Resistencia al cizallamiento | 23.0 °C | 114 MPa Show Supplier Material materials with Resistencia al cizallamiento of 114 MPa | ASTM D732 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2E-6 1/K | ASTM E 831 | -40°C to 150°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 2E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 2E-5 1/K | ASTM E 831 | -40°C to 150°C |
Heat deflection temperature, 1.80 MPa | 335 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 335 °C | ASTM D 648 | 3.2mm, unannealed | |
Temperatura de flexión bajo carga | 335 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 335 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 1000 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 150°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |