Propiedades
General
| Property | Temperature | Value | Comment |
|---|---|---|---|
Densidad | 23.0 °C | 1.32 g/cm³ Show Supplier Material materials with Densidad of 1.32 g/cm³ | ISO 1183 |
Mecánica
| Property | Temperature | Value | Comment |
|---|---|---|---|
Flexural strain | 23.0 °C | 2.5 % Show Supplier Material materials with Flexural strain of 2.5 % | ISO 178 | break, 2 mm/min |
Módulo de flexión | 23.0 °C | 5.8 GPa Show Supplier Material materials with Módulo de flexión of 5.8 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 6.2 GPa Show Supplier Material materials with Módulo elástico of 6.2 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 130 MPa Show Supplier Material materials with Resistencia a la flexión of 130 MPa | ISO 178 | break, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 85 MPa Show Supplier Material materials with Resistencia a la tracción of 85 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 23 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 23 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Aplicaciones térmicas
| Property | Value | Comment | |
|---|---|---|---|
Glow Wire Flammability Index | 960 °C Show Supplier Material materials with Glow Wire Flammability Index of 960 °C | ||
Glow Wire Ignition Temperature | 825 °C Show Supplier Material materials with Glow Wire Ignition Temperature of 825 °C | IEC 60695-2-13 | 2.0 mm | |
Heat deflection temperature, 1.80 MPa | 118 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 118 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm | |
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |
Temperatura de flexión bajo carga | 118 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 118 °C | ||
Temperatura de reblandecimiento Vicat | 130 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 130 °C | ISO 306 | Rate B/120 | |
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=101284052- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 <br> Glow Wire Ignitability Temperature, 1.5 mm: 825°C IEC 60695-2-13 <br> Glow Wire Flammability Index, 1.5 mm: 960°C IEC 60695-2-12 | ||
Eléctrico
| Property | Temperature | Value | Comment |
|---|---|---|---|
Índice de seguimiento comparativo | 23.0 °C | 4 V Show Supplier Material materials with Índice de seguimiento comparativo of 4 V | UL 746A | (UL) {PLC} |
Rheological Properties
| Property | Temperature | Value | Comment |
|---|---|---|---|
Contracción | 23.0 °C | 0.2 % Show Supplier Material materials with Contracción of 0.2 % | SABIC method |
Contracción transversal | 23.0 °C | 0.3 % Show Supplier Material materials with Contracción transversal of 0.3 % | SABIC method |
Velocidad de flujo del volumen derretido | 8 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 8 cm³/10min | ISO 1133 | MVR at 260°C/5.0 kg |
Technological properties
| Property | ||
|---|---|---|
| Application areas | Enclosures | |
| Availability | Europe,Asia,Americas | |
| Processing methods | Drying Temperature: 80 to 90.0°C | |
| Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. | |