General
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 4 % Show Supplier Material materials with Elongación of 4 % | ASTM D 638 | brk, Type I, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 122 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 122 J/m | ASTM D 256 |
Módulo de flexión | 23.0 °C | 6.6 GPa Show Supplier Material materials with Módulo de flexión of 6.6 GPa | ASTM D 790 | 1.3 mm/min, 50 mm span |
Resistencia a la flexión | 23.0 °C | 147 MPa Show Supplier Material materials with Resistencia a la flexión of 147 MPa | ASTM D 790 | brk, 1.3 mm/min, 50 mm span |
Resistencia a la tracción | 23.0 °C | 117 MPa Show Supplier Material materials with Resistencia a la tracción of 117 MPa | ASTM D 638 | brk, Type I, 50 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 122 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 122 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment | ||
---|---|---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.7E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.7E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Coeficiente de dilatación térmica transversal | 23.0 °C | 4.68E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 4.68E-5 1/K | ASTM D 696 | -30°C to 30°C | ||
Heat deflection temperature, 1.80 MPa | 146 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 146 °C | ASTM D 648 | 6.4 mm, unannealed | |||
Relative temperature index, electrical | 80 °C Show Supplier Material materials with Relative temperature index, electrical of 80 °C | UL 746B | |||
Relative temperature index, mechanical impact | 80 °C Show Supplier Material materials with Relative temperature index, mechanical impact of 80 °C | UL 746B | |||
Relative temperature index, mechanical strength | 80 °C Show Supplier Material materials with Relative temperature index, mechanical strength of 80 °C | UL 746B | |||
Temperatura de flexión bajo carga | 146 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 146 °C | ||||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228440- - <br> UL Yellow Card Link 2: https://iq.ul.com/ul/cert.aspx?ULID=236909- - <br> UL Recognized, 94V-0 Flame Class Rating: ≥1.5mm UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
High Amp Arc Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with High Amp Arc Ignition of 1.5 mm | UL 746A | PLC 4 |
Hot-Wire Ignition | 23.0 °C | 1.5 mm Show Supplier Material materials with Hot-Wire Ignition of 1.5 mm | UL 746A | PLC 0 |
Rigidez dieléctrica | 23.0 °C | 17.7 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 17.7 kV/mm | ASTM D 149 | in oil, 3.2 mm |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Electronic Components, Document Handling, Pharmaceutical Packaging & Drug Delivery | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |