General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad relativa | 23.0 °C | 1.21 [-] Show Supplier Material materials with Densidad relativa of 1.21 [-] | ASTM D 792 | |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 200 % Show Supplier Material materials with Elongación of 200 % | ISO 527 | break, 50 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 700 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 700 J/m | ASTM D 256 |
Módulo de flexión | 23.0 °C | 2 GPa Show Supplier Material materials with Módulo de flexión of 2 GPa | ASTM D 790 |
Resistencia a la flexión | 23.0 °C | 80 MPa Show Supplier Material materials with Resistencia a la flexión of 80 MPa | ASTM D 790 | yield, 6.4 mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 700 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 700 kJ/m² | ASTM D 256 | notched, 23°C |
Aplicaciones térmicas
Property | Value | Comment | |
---|---|---|---|
Heat deflection temperature, 1.80 MPa | 100 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 100 °C | ASTM D 648 | 6.4 mm, unannealed | |
Temperatura de flexión bajo carga | 100 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 100 °C | ||
Inflamabilidad | UL Yellow Card Link: https://iq.ul.com/ul/cert.aspx?ULID=228454- - <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94V-2 Flame Class Rating: ≥1mm UL 94 <br> UL Recognized, 94HB Flame Class Rating: ≥0.5mm UL 94 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 1.20E+12 Ω Show Supplier Material materials with Sheet resistivity, ROA of 1.20E+12 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción of 0.4 % | SABIC method | 1.5-3.2 mm |
Contracción transversal | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción transversal of 0.5 % | SABIC method | 1.5-3.2 mm |
Velocidad de flujo de la masa derretida | 19 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 19 g/10min | ASTM D 1238 | 260°C/2.16 kgf |
Technological properties
Property | ||
---|---|---|
Application areas | Personal Computing, Pallet, Photo/Video Camera, Data Management, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 90 to 100.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |