General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.236 g/cm³ Show Supplier Material materials with Densidad of 1.236 g/cm³ | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 16.5 % Show Supplier Material materials with Elongación of 16.5 % | ISO 527 | break, 5 mm/min |
Flexural strain | 23.0 °C | 7.8 % Show Supplier Material materials with Flexural strain of 7.8 % | ISO 178 | break, 2 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 359 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 359 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 2140 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 2140 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 39 J Show Supplier Material materials with Instrumented Impact, Total Energy of 39 J | ASTM D 3763 | 23°C |
Instrumented Impact, at Peak | 23.0 °C | 27 J Show Supplier Material materials with Instrumented Impact, at Peak of 27 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo de flexión of 2.6 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 2.6 GPa Show Supplier Material materials with Módulo elástico of 2.6 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 92 MPa Show Supplier Material materials with Resistencia a la flexión of 92 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 58 MPa Show Supplier Material materials with Resistencia a la tracción of 58 MPa | ISO 527 | yield, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 26 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 26 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm, 23°C |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 24 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 24 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 130 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 130 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Value | Comment |
---|---|---|
Heat deflection temperature, 1.80 MPa | 126 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 126 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Temperatura de flexión bajo carga | 126 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 126 °C | |
Temperatura de reblandecimiento Vicat | 144 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 144 °C | ISO 306 | Rate A/50 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 4.80E+7 Ω Show Supplier Material materials with Sheet resistivity, ROA of 4.80E+7 Ω | ASTM D 257 |
Volume resistivity | 23.0 °C | 1.41E+7 Ω·cm Show Supplier Material materials with Volume resistivity of 1.41E+7 Ω·cm | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.64 % Show Supplier Material materials with Contracción of 0.64 % | SABIC method | 1.5-3.2 mm |
Contracción transversal | 23.0 °C | 0.68 % Show Supplier Material materials with Contracción transversal of 0.68 % | SABIC method | 1.5-3.2 mm |
Velocidad de flujo del volumen derretido | 16 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 16 cm³/10min | ISO 1133 | MVR at 300°C/5.0 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Semiconductor, LED Lighting, Enclosures, Electronic Components | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |