General
Property | Temperature | Value | Comment |
---|---|---|---|
Densidad | 23.0 °C | 1.44 g/cm³ Show Supplier Material materials with Densidad of 1.44 g/cm³ | ASTM D 792 |
Densidad relativa | 23.0 °C | 1.45 [-] Show Supplier Material materials with Densidad relativa of 1.45 [-] | ASTM D 792 | |
Moisture absorption | 23.0 °C | 0.02 % Show Supplier Material materials with Moisture absorption of 0.02 % | ISO 62 | (23°C / 50% RH) |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1 % Show Supplier Material materials with Elongación of 1 % | ISO 527 | break, 5 mm/min |
Impact strength, Izod notched, ASTM | 23.0 °C | 49 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 49 J/m | ASTM D 256 | notched, 23°C |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 442 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 442 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 9 J Show Supplier Material materials with Instrumented Impact, Total Energy of 9 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 19.6 GPa Show Supplier Material materials with Módulo de flexión of 19.6 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 22 GPa Show Supplier Material materials with Módulo elástico of 22 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 263 MPa Show Supplier Material materials with Resistencia a la flexión of 263 MPa | ISO 178 |
Resistencia a la tracción | 23.0 °C | 173 MPa Show Supplier Material materials with Resistencia a la tracción of 173 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 5 kJ/m² | ISO 180/1A | notched 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 30 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 30 kJ/m² | ISO 180/1U | unnotched 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8E-6 1/K | ASTM D 696 | -30°C to 30°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 3.5E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 3.5E-5 1/K | ASTM D 696 | -30°C to 30°C |
Heat deflection temperature, 0.45 MPa | 275 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 275 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm | |
Heat deflection temperature, 1.80 MPa | 252 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 252 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 252 - 275 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 252 - 275 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 100 - 100000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 100 - 100000 Ω | ASTM D 257 |
Rheological Properties
Technological properties
Property | ||
---|---|---|
Application areas | Lab Ware and Clinical Diagnostics, Air Cabin Interiors | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |