General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.26 % Show Supplier Material materials with Absorción de agua of 0.26 % | ISO 62-1 | (23°C/saturated) |
Densidad | 23.0 °C | 1.53 g/cm³ Show Supplier Material materials with Densidad of 1.53 g/cm³ | ISO 1183 |
Densidad relativa | 23.0 °C | 1.53 [-] Show Supplier Material materials with Densidad relativa of 1.53 [-] | ASTM D 792 |
Moisture absorption | 23.0 °C | 0.06 % Show Supplier Material materials with Moisture absorption of 0.06 % | ISO 62 | (23°C / 50% RH) |
Specific volume | 23.0 °C | 0.66 cm³/g Show Supplier Material materials with Specific volume of 0.66 cm³/g | ASTM D 792 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 2 % Show Supplier Material materials with Elongación of 2 % | ISO 527 | break, 5 mm/min |
Hardness, Rockwell R | 23.0 °C | 118 [-] Show Supplier Material materials with Hardness, Rockwell R of 118 [-] | ASTM D 785 |
Impact strength, Izod notched, ASTM | 23.0 °C | 85 J/m Show Supplier Material materials with Impact strength, Izod notched, ASTM of 85 J/m | ASTM D 256 |
Impact strength, Izod unnotched, ASTM | 23.0 °C | 801 J/m Show Supplier Material materials with Impact strength, Izod unnotched, ASTM of 801 J/m | ASTM D 4812 | 23°C |
Instrumented Impact, Total Energy | 23.0 °C | 10 J Show Supplier Material materials with Instrumented Impact, Total Energy of 10 J | ASTM D 3763 | 23°C |
Módulo de flexión | 23.0 °C | 8.5 GPa Show Supplier Material materials with Módulo de flexión of 8.5 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 9.3 GPa Show Supplier Material materials with Módulo elástico of 9.3 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 195 MPa Show Supplier Material materials with Resistencia a la flexión of 195 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 125 MPa Show Supplier Material materials with Resistencia a la tracción of 125 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Charpy entallado | 23.0 °C | 5 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Charpy entallado of 5 kJ/m² | ISO 179/1eA | V-notch Edgew, 23°C, 80*10*4 sp=62mm |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 8 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 8 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 45 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 45 kJ/m² | ISO 180/1U | 80*10*4, 23°C |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 2.52E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 2.52E-5 1/K | ISO 11359-2 | -40°C to 40°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 1.2E-4 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 1.2E-4 1/K | ISO 11359-2 | -40°C to 40°C |
Heat deflection temperature, 0.45 MPa | 215 °C Show Supplier Material materials with Heat deflection temperature, 0.45 MPa of 215 °C | ASTM D 648 | 6.4 mm, unannealed | |
Heat deflection temperature, 1.80 MPa | 200 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 200 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 200 - 215 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 200 - 215 °C | ||
Temperatura de reblandecimiento Vicat | 215 °C Show Supplier Material materials with Temperatura de reblandecimiento Vicat of 215 °C | ISO 306 | Rate B/50 |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Constante dieléctrica, 1 MHz | 23.0 °C | 3.7 [-] Show Supplier Material materials with Constante dieléctrica, 1 MHz of 3.7 [-] | ASTM D 150 |
Constante dieléctrica, 100 Hz | 23.0 °C | 3.8 [-] Show Supplier Material materials with Constante dieléctrica, 100 Hz of 3.8 [-] | ASTM D 150 |
Dissipation factor, 100Hz | 23.0 °C | 2E-3 [-] Show Supplier Material materials with Dissipation factor, 100Hz of 2E-3 [-] | ASTM D 150 |
Dissipation factor, 1MHz | 23.0 °C | 0.02 [-] Show Supplier Material materials with Dissipation factor, 1MHz of 0.02 [-] | ASTM D 150 |
Rigidez dieléctrica | 23.0 °C | 24.8 kV/mm Show Supplier Material materials with Rigidez dieléctrica of 24.8 kV/mm | ASTM D 149 | in oil, 1.6 mm |
Volume resistivity | 23.0 °C | 3.20E+16 Ω·cm Show Supplier Material materials with Volume resistivity of 3.20E+16 Ω·cm | >, ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.5 % Show Supplier Material materials with Contracción of 0.5 % | |
Contracción transversal | 23.0 °C | 0.4 % Show Supplier Material materials with Contracción transversal of 0.4 % | SABIC method | 1.5-3.2 mm |
Velocidad de flujo de la masa derretida | 17 g/10min Show Supplier Material materials with Velocidad de flujo de la masa derretida of 17 g/10min | ASTM D 1238 | 250°C/2.16 kgf | |
Velocidad de flujo del volumen derretido | 13 cm³/10min Show Supplier Material materials with Velocidad de flujo del volumen derretido of 13 cm³/10min | ISO 1133 | MVR at 250°C/2.16 kg |
Technological properties
Property | ||
---|---|---|
Application areas | Pharmaceutical Packaging & Drug Delivery | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |