General
Property | Temperature | Value | Comment |
---|---|---|---|
Absorción de agua | 23.0 °C | 0.4 % Show Supplier Material materials with Absorción de agua of 0.4 % | ISO 62-1 | (23°C/24hrs) |
Coefficient of friction | 0.33 - 0.62 [-] Show Supplier Material materials with Coefficient of friction of 0.33 - 0.62 [-] | ||
Coefficient of friction, kinetic | 0.33 [-] Show Supplier Material materials with Coefficient of friction, kinetic of 0.33 [-] | ASTM D 3702 Modified: Instr. | |
Coefficient of friction, static | 0.62 [-] Show Supplier Material materials with Coefficient of friction, static of 0.62 [-] | ASTM D 3702 Modified: Instr. | |
Densidad | 23.0 °C | 1.42 g/cm³ Show Supplier Material materials with Densidad of 1.42 g/cm³ | ISO 1183 |
Mecánica
Property | Temperature | Value | Comment |
---|---|---|---|
Elongación | 23.0 °C | 1.3 % Show Supplier Material materials with Elongación of 1.3 % | ISO 527 | break, 5 mm/min |
Módulo de flexión | 23.0 °C | 19.9 GPa Show Supplier Material materials with Módulo de flexión of 19.9 GPa | ISO 178 | 2 mm/min |
Módulo elástico | 23.0 °C | 25.1 GPa Show Supplier Material materials with Módulo elástico of 25.1 GPa | ISO 527 | 1 mm/min |
Resistencia a la flexión | 23.0 °C | 340 MPa Show Supplier Material materials with Resistencia a la flexión of 340 MPa | ISO 178 | yield, 2 mm/min |
Resistencia a la tracción | 23.0 °C | 256 MPa Show Supplier Material materials with Resistencia a la tracción of 256 MPa | ISO 527 | break, 5 mm/min |
Resistencia al choque, ensayo Izod entallado | 23.0 °C | 7 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod entallado of 7 kJ/m² | ISO 180/1A | 80*10*4, 23°C |
Resistencia al choque, ensayo Izod no entallado | 23.0 °C | 40 kJ/m² Show Supplier Material materials with Resistencia al choque, ensayo Izod no entallado of 40 kJ/m² | ISO 180/1U | unnotched 80*10*4 |
Aplicaciones térmicas
Property | Temperature | Value | Comment |
---|---|---|---|
Coeficiente de dilatación térmica | 23.0 °C | 8E-6 1/K Show Supplier Material materials with Coeficiente de dilatación térmica of 8E-6 1/K | ISO 11359-2 | 23°C to 60°C |
Coeficiente de dilatación térmica transversal | 23.0 °C | 5.1E-5 1/K Show Supplier Material materials with Coeficiente de dilatación térmica transversal of 5.1E-5 1/K | ISO 11359-2 | 23°C to 60°C |
Heat deflection temperature, 1.80 MPa | 270 °C Show Supplier Material materials with Heat deflection temperature, 1.80 MPa of 270 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm | |
Temperatura de flexión bajo carga | 270 °C Show Supplier Material materials with Temperatura de flexión bajo carga of 270 °C |
Eléctrico
Property | Temperature | Value | Comment |
---|---|---|---|
Sheet resistivity, ROA | 23.0 °C | 10 - 1000 Ω Show Supplier Material materials with Sheet resistivity, ROA of 10 - 1000 Ω | ASTM D 257 |
Rheological Properties
Property | Temperature | Value | Comment |
---|---|---|---|
Contracción | 23.0 °C | 0.05 % Show Supplier Material materials with Contracción of 0.05 % | SABIC method |
Technological properties
Property | ||
---|---|---|
Application areas | Sensor, Heavy Vehicles, Gear/Bearing/Slider, Lawn/Garden, EV Infrastructure, Electronic Components, Auto Aftermarket | |
Availability | Europe,Asia,Americas | |
Processing methods | Drying Temperature: 120 to 150.0°C | |
Supplier Disclaimer | While the information is provided in good faith, SABIC MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Buyer must determine the suitability of SABIC's materials for the Buyer's particular use through appropriate testing and analysis. No statement by SABIC concerning a possible use of any product, service or design is intended, or should be construed, to grant any license under any patent or other intellectual property right. |